Production of Structural Particleboard of Mimosa Scabrella Benth With Lignin Phenol-formaldehyde Resin
Tipo de material:
ArtigoAssunto(s): Recursos online:
Em: Floresta e Ambiente (Brazil) v. 26(3) p. 1-8; (2019)Sumário:
ABSTRACT
The objective of this work was to evaluate the feasibility of using lignin-phenol-formaldehyde
resin in the production of Mimosa scabrella Benth (bracatinga) structural particleboard.
The boards were produced with nominal specific mass of 0.75 and 0.95 g/cm3, 10% and 12% of
phenol-formaldehyde and lignin-phenol-formaldehyde resins, with 10 and 12 min of pressing
time. The boards quality was evaluated by means of the following physical-mechanical tests:
specific mass, compression ratio, water absorption and thickness swelling after 2 and 24 hours
soaking, perpendicular traction, static bending and screw pulling. Positive interactions of
specific mass, resin content and pressing time were observed in the properties of the boards
produced. The evaluation of the properties results based on the requirements of EN 312 (type P5)
standard indicated the feasibility of using lignin-phenol-formaldehyde resin in the production
of particleboard of Mimosa scabrellla for structural applications.
Keywords: phenolic resin, bracatinga, structural boards.
Produção de painel aglomerado estrutural de Mimosa scabrella Benth com resina lignina-fenol-formaldeído
RESUMO
O objetivo do trabalho foi avaliar a viabilidade de uso da resina lignina-fenol-formaldeído na
produção de painel aglomerado estrutural de Mimosa scabrella Benth (bracatinga). Os painéis
foram produzidos com massa específica nominal de 750 kg.m-3 e 950 kg.m-3, 10 e 12% de resina
fenol-formaldeído e lignina-fenol-formaldeído, e 10 e 12 minutos de prensagem. A qualidade
dos painéis experimentais foi avaliada por meio de seguintes ensaios físico-mecânicos: massa
específica, razão de compactação, absorção de água e inchamento em espessura 2 e 24 horas,
tração perpendicular, flexão estática e arrancamento de parafuso. Foram constatadas interações
positivas da massa específica, teor de resina e tempo de prensagem nas propriedades dos painéis
produzidos. A avaliação dos resultados das propriedades com base nos requisitos da norma
EN 312:2003 (tipo P5), indicaram a viabilidade de uso da resina lignina-fenol-formaldeído na
produção de painel aglomerado de Mimosa scabrellla para aplicações estruturais.
Palavras-chave: resina fenólica, bracatinga, painéis estruturais.
| Tipo de material | Biblioteca atual | Coleção | Número de chamada | Informaçaõ do volume | Situação | Devolução em | Código de barras |
|---|---|---|---|---|---|---|---|
Periódicos
|
Biblioteca Nacional de Agricultura - Binagri Agrobase - Periódicos | Periódicos agrícolas | 2019 26(3) | Online | 2025-0451 |
Publicação on-line; 15 ref.; 6 tables; Summary (En)
ABSTRACT
The objective of this work was to evaluate the feasibility of using lignin-phenol-formaldehyde
resin in the production of Mimosa scabrella Benth (bracatinga) structural particleboard.
The boards were produced with nominal specific mass of 0.75 and 0.95 g/cm3, 10% and 12% of
phenol-formaldehyde and lignin-phenol-formaldehyde resins, with 10 and 12 min of pressing
time. The boards quality was evaluated by means of the following physical-mechanical tests:
specific mass, compression ratio, water absorption and thickness swelling after 2 and 24 hours
soaking, perpendicular traction, static bending and screw pulling. Positive interactions of
specific mass, resin content and pressing time were observed in the properties of the boards
produced. The evaluation of the properties results based on the requirements of EN 312 (type P5)
standard indicated the feasibility of using lignin-phenol-formaldehyde resin in the production
of particleboard of Mimosa scabrellla for structural applications.
Keywords: phenolic resin, bracatinga, structural boards.
Produção de painel aglomerado estrutural de Mimosa scabrella Benth com resina lignina-fenol-formaldeído
RESUMO
O objetivo do trabalho foi avaliar a viabilidade de uso da resina lignina-fenol-formaldeído na
produção de painel aglomerado estrutural de Mimosa scabrella Benth (bracatinga). Os painéis
foram produzidos com massa específica nominal de 750 kg.m-3 e 950 kg.m-3, 10 e 12% de resina
fenol-formaldeído e lignina-fenol-formaldeído, e 10 e 12 minutos de prensagem. A qualidade
dos painéis experimentais foi avaliada por meio de seguintes ensaios físico-mecânicos: massa
específica, razão de compactação, absorção de água e inchamento em espessura 2 e 24 horas,
tração perpendicular, flexão estática e arrancamento de parafuso. Foram constatadas interações
positivas da massa específica, teor de resina e tempo de prensagem nas propriedades dos painéis
produzidos. A avaliação dos resultados das propriedades com base nos requisitos da norma
EN 312:2003 (tipo P5), indicaram a viabilidade de uso da resina lignina-fenol-formaldeído na
produção de painel aglomerado de Mimosa scabrellla para aplicações estruturais.
Palavras-chave: resina fenólica, bracatinga, painéis estruturais.