245			_aCorrosividade Causada por Soluções Salinas Empregadas na Estabilização Dimensional da Madeira
500			_aPublicação on-line; 19 ref.; 4 tables; Summaries (En, Pt)
520			_a RESUMO Objetivou-se avaliar a corrosividade de soluções salinas antes e depois de sua impregnação na madeira. Soluções com 5% de concentração de cloreto de lítio, carbonato de sódio, sulfato de magnésio, sulfato de zinco e sulfato de cobre II foram mantidas durante 6 horas, a 25 °C, 45 °C e 100 °C em contato com amostras de 1,25 cm × 0,1 cm × 7,5 cm (largura × espessura × comprimento) produzidas com chapas de aço carbono antes e depois de seu contato com amostras de madeira de Corymbia torelliana e Eucalyptus cloeziana. Não se observou efeito da temperatura na corrosão das soluções puras. Depois do contato com a madeira houve incremento da corrosividade para as soluções de sulfato de zinco e de cobre II. O sulfato de cobre II ocasionou a maior perda de massa nas chapas, não sendo recomendado seu contato com superfícies metálicas, como usinas de tratamento e câmaras de secagem de madeira. Palavras-chave: corrosão, soluções salinas, extrativos, madeira. Corrosivity Caused by Salt Solutions Employed in the Wood Dimensional Stability ABSTRACT The study aimed to evaluate the corrosivity of salt solutions after and before the impregnation in the wood. Solutions with concentration of 5% of chloride of lithium, sodium carbonate, magnesium sulphate, zinc sulphate and copper sulphate II had been kept during 6 hours, at 25; 45 and 100 °C, in contact with steel plates carbon samples of 1.25 × 0.1 × 7.5 cm (width × thickness × length), before and after its contact with wood samples of Corymbia torelliana and Eucalyptus cloeziana. There was no effect of the temperature in the corrosion of the pure solutions. After the contact with woods, corrosivity was incremented with copper II and zinc sulphate solutions. Copper II sulphate caused the biggest loss of mass in plates, and its contact with metallic surfaces is not recommended as wood treatment and drying chambers. Keywords: corrosion, salt solutions, extractives, wood.
650			_aCORROSÃO
650			_aSOLUÇÃO
650			_aSALINA
650			_aMADEIRA
773	0		_02929 _9347945 _dRio de Janeiro-RJ Instituto de Florestas - UFRRJ 1994 _o2025-0444 _tFloresta e Ambiente (Brazil) _x1415-0980 / ISSN 2179-8087 0nline _gv. 24 p. 1-6; (2017) _wBR2026000244
856			_uhttps://www.scielo.br/j/floram/a/JfY8VHSkHJRywS3DZ7p8hcT/?format=pdf&lang=pt
942			_cANA
999			_c340480 _d340480